| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | 300°C/10.0kg | ASTM D1238 | 33 g/10min |
| melt mass-flow rate | 300°C/5.0kg | ASTM D1238 | 11 g/10min |
| Melt volume flow rate | 300°C/10.0kg | ISO 1133 | 31.0 cm³/10min |
| Melt volume flow rate | 300°C/5.0kg | ISO 1133 | 10.0 cm³/10min |
| Shrinkage rate | TD:24小时 | ISO 294-4 | 0.70to0.90 % |
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.70to0.90 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.050 % |
| density | | ISO 1183 | 1.21 g/cm³ |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.030mm | UL 94 | HB |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C8 | ISO 180/1A | 55 kJ/m² |
| Impact strength of cantilever beam gap | -20°C | ASTM D256 | 140 J/m |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 720 J/m |
| Impact strength of cantilever beam gap | -20°C8 | ISO 180/1A | 13 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | --2 | ASTM D638 | 2290 MPa |
| Tensile modulus | -- | ISO 527-2/1 | 2240 MPa |
| tensile strength | 屈服3 | ASTM D638 | 58.0 MPa |
| tensile strength | Yield | ISO 527-2/50 | 57.0 MPa |
| tensile strength | 断裂3 | ASTM D638 | 51.0 MPa |
| tensile strength | Break | ISO 527-2/50 | 49.0 MPa |
| elongation | 屈服3 | ASTM D638 | 9.0 % |
| elongation | Yield | ISO 527-2/50 | 8.9 % |
| elongation | 断裂3 | ASTM D638 | 34 % |
| elongation | Break | ISO 527-2/50 | 33 % |
| Flexural modulus | 50.0mm跨距4 | ASTM D790 | 2080 MPa |
| Flexural modulus | --5 | ISO 178 | 2210 MPa |
| bending strength | --5,6 | ISO 178 | 93.0 MPa |
| bending strength | --5,7 | ISO 178 | 91.0 MPa |
| bending strength | 屈服,50.0mm跨距4 | ASTM D790 | 86.0 MPa |
| bending strength | 断裂,50.0mm跨距4 | ASTM D790 | 84.0 MPa |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| dielectric constant | 10.0GHz | 内部方法 | 3.06 |
| Dissipation Factor | 1.10GHz | 内部方法 | 9E-04 |
| Dissipation Factor | 1.90GHz | 内部方法 | 1.1E-03 |
| Dissipation Factor | 5.00GHz | 内部方法 | 1.4E-03 |
| Dissipation Factor | 10.0GHz | 内部方法 | 2E-03 |
| dielectric constant | 1.10GHz | 内部方法 | 3.04 |
| dielectric constant | 1.90GHz | 内部方法 | 3.05 |
| dielectric constant | 5.00GHz | 内部方法 | 3.06 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 174 °C |
| Heat distortion temperature | 0.45MPa,未退火,64.0mm跨距9，HDT | ISO 75-2/Bf | 175 °C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 154 °C |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距9，HDT | ISO 75-2/Af | 155 °C |
| Linear coefficient of thermal expansion | MD:-40到150°C | ASTME831 | 6.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD:-40到150°C | ASTME831 | 9.4E-05 cm/cm/°C |