PPO(PPE)+SEBS LNP™ THERMOCOMP™ ZKC04 compound SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC/LNP™ THERMOCOMP™ ZKC04 compound
Impact strength of cantilever beam gap23°CASTM D256720 J/m
23°C8ISO 180/1A55 kJ/m²
-20°CASTM D256140 J/m
-20°C8ISO 180/1A13 kJ/m²
Electrical performanceTest ConditionTest MethodSABIC/LNP™ THERMOCOMP™ ZKC04 compound
dielectric constant1.90GHz内部方法3.05
Dissipation Factor5.00GHz内部方法1.4E-03
1.90GHz内部方法1.1E-03
10.0GHz内部方法2E-03
dielectric constant1.10GHz内部方法3.04
Dissipation Factor1.10GHz内部方法9E-04
dielectric constant10.0GHz内部方法3.06
5.00GHz内部方法3.06
Mechanical propertiesTest ConditionTest MethodSABIC/LNP™ THERMOCOMP™ ZKC04 compound
tensile strength 屈服3ASTM D63858.0 MPa
elongation断裂3ASTM D63834 %
断裂ISO 527-2/5033 %
Flexural modulus--5ISO 1782210 MPa
bending strength断裂,50.0mm跨距4ASTM D79084.0 MPa
Tensile modulus--ISO 527-2/12240 MPa
bending strength屈服,50.0mm跨距4ASTM D79086.0 MPa
tensile strength 屈服ISO 527-2/5057.0 MPa
Flexural modulus50.0mm跨距4ASTM D7902080 MPa
bending strength--5,7ISO 17891.0 MPa
--5,6ISO 17893.0 MPa
elongation屈服ISO 527-2/508.9 %
屈服3ASTM D6389.0 %
tensile strength 断裂3ASTM D63851.0 MPa
Tensile modulus--2ASTM D6382290 MPa
tensile strength 断裂ISO 527-2/5049.0 MPa
flammabilityTest ConditionTest MethodSABIC/LNP™ THERMOCOMP™ ZKC04 compound
UL flame retardant rating1.030mmUL 94HB
physical property Test ConditionTest MethodSABIC/LNP™ THERMOCOMP™ ZKC04 compound
Melt volume flow rate300°C/5.0kgISO 113310.0 cm³/10min
Shrinkage rateMD:24小时ISO 294-40.70to0.90 %
melt mass-flow rate300°C/5.0kgASTM D123811 g/10min
Water absorption rate23°C,24hrISO 620.050 %
Melt volume flow rate300°C/10.0kgISO 113331.0 cm³/10min
Shrinkage rateTD:24小时ISO 294-40.70to0.90 %
densityISO 11831.21 g/cm³
melt mass-flow rate300°C/10.0kgASTM D123833 g/10min
Thermal performanceTest ConditionTest MethodSABIC/LNP™ THERMOCOMP™ ZKC04 compound
Heat distortion temperature0.45MPa,未退火,64.0mm跨距9，HDTISO 75-2/Bf175 °C
Linear coefficient of thermal expansionMD:-40到150°CASTME8316.5E-05 cm/cm/°C
TD:-40到150°CASTME8319.4E-05 cm/cm/°C
Heat distortion temperature0.45MPa,未退火,3.20mm，HDTASTM D648174 °C
1.8MPa,未退火,64.0mm跨距9，HDTISO 75-2/Af155 °C
1.8MPa,未退火,3.20mm，HDTASTM D648154 °C