impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	-40°C	ISO 179/1eA	5.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	22 kJ/m²

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot filament ignition temperature	1.50mm	IEC 60695-2-13	725 °C
Burning wire flammability index	3.00mm	IEC 60695-2-12	700 °C
Burning wire flammability index	Burning wire flammability index	1.50mm	IEC 60695-2-12	700 °C
UL flame retardant rating	3.20mm	UL 94,IEC60695-11-10,-20	HB
UL flame retardant rating	UL flame retardant rating	1.60mm	UL 94,IEC60695-11-10,-20	HB
Burning rate	2.00mm	ISO 3795	<100 mm/min
Hot filament ignition temperature	3.00mm	IEC 60695-2-13	725 °C

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
bending strength	9.0%Strain	ISO 178	60.0 MPa
bending strength	bending strength	3.5%Strain	ISO 178	60.0 MPa
Bending modulus		ISO 178	1500 MPa
Tensile strain	Yield	ISO 527-2/1A/50	20 %
tensile strength	Yield	ISO 527-2/1A/50	60.0 MPa
Tensile modulus		ISO 527-2/1A/1	1400 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Vicat softening temperature		ISO 306/B50	191 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	100 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Melt Volume Flow Rate (MVR)	240°C/2.16kg	ISO 1133	6.00 cm³/10min
density		ISO 1183/A	1.24 g/cm³