PK SCHULAKETON MV A SCHULMAN USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON MV |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 22 kJ/m² |
-40°C | ISO 179/1eA | 5.0 kJ/m² |
Mechanical properties | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON MV |
---|---|---|---|
Tensile strain | 屈服 | ISO 527-2/1A/50 | 20 % |
Tensile modulus | ISO 527-2/1A/1 | 1400 MPa | |
bending strength | 3.5%应变 | ISO 178 | 60.0 MPa |
Flexural modulus | ISO 178 | 1500 MPa | |
tensile strength | 屈服 | ISO 527-2/1A/50 | 60.0 MPa |
bending strength | 9.0%应变 | ISO 178 | 60.0 MPa |
flammability | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON MV |
---|---|---|---|
Hot filament ignition temperature | 1.50mm | IEC 60695-2-13 | 725 °C |
UL flame retardant rating | 1.60mm | UL 94,IEC60695-11-10,-20 | HB |
Hot filament ignition temperature | 3.00mm | IEC 60695-2-13 | 725 °C |
burning rate | 2.00mm | ISO 3795 | <100 mm/min |
UL flame retardant rating | 3.20mm | UL 94,IEC60695-11-10,-20 | HB |
Burning wire flammability index | 3.00mm | IEC 60695-2-12 | 700 °C |
1.50mm | IEC 60695-2-12 | 700 °C |
physical property | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON MV |
---|---|---|---|
Melt volume flow rate | 240°C/2.16kg | ISO 1133 | 6.00 cm³/10min |
density | ISO 1183/A | 1.24 g/cm³ |
Thermal performance | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON MV |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/Af | 100 °C |
vicat | ISO 306/B50 | 191 °C |