برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shrinkage rate | TD | ISO 294-4 | 0.80 % |
| Shrinkage rate | MD | ISO 294-4 | 0.30 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | <0.020 % |
| processability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shrinkage rate | 流动方向 | ASTM D-955 | 0.3 % |
| Shrinkage rate | 垂直方向 | ASTM D-955 | 0.7 % |
| Dry conditions | | | 120-150度 2.0-5.0hr |
| process temperature | | | 270-300 °C |
| process temperature | | | 290-330 °C |
| screw speed | | | 100-150 rpm |
| Temperature | | | 135-150 °C |
| pressure | | | 1.00-20.0 Mpa |
| other | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| characteristic | | | 韧性良好 |
| Color | | | 黑色 |
| purpose | | | 注射型 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| BarFlowLength | | 内部方法 | 175 mm |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| elongation at break | | ASTM D-638 | 1.7 % |
| tensile strength | | ASTM D-638 | 172 Mpa |
| Charpy Notched Impact Strength | 有缺口 | ASTM D-256 | 74 J/m |
| Charpy Notched Impact Strength | 无缺口 | ASTM D-256 | 541 J/m |
| Rockwell hardness | | ASTM D-785 | 122 |
| bending strength | | ASTM D-790 | 275 Mpa |
| Flexural modulus | | ASTM D-790 | 15 GPa |
| tensile strength | 屈服 | ISO 527-2 | 176 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 1.5 % |
| Flexural modulus | | ISO 178 | 14700 Mpa |
| bending strength | | ISO 178 | 275 Mpa |
| Tensile Weld Strength | | 内部方法 | 60.0 Mpa |
| Impact strength of cantilever beam gap | | ASTM D256/ISO 179 | 82 kg·cm/cm(J/M)ft·lb/in |
| elongation at break | | ASTM D638/ISO 527 | 1.5 % |
| tensile strength | | ASTM D638/ISO 527 | 176 kg/cm²(MPa)[Lb/in²] |
| Flexural modulus | | ASTM D790/ISO 178 | 14700 kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 275 kg/cm²(MPa)[Lb/in²] |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ASTM D-257 | 4×1016 Ω.cm |
| dielectric constant | 1MHz | ASTM D-150 | 3.9 |
| Dissipation Factor | 1MHz | ASTM D-150 | 0.0014 |
| dielectric strength | | ASTM D-149 | 16 KV/mm |
| thermal conductivity | | 自定标准 | 0.27 W/m.K |
| Volume resistivity | | IEC 60093 | 1E+17 ohms·cm |
| dielectric strength | | IEC 60243-1 | 16 KV/mm |
| dielectric constant | 1MHz | IEC 60250 | 3.90 |
| Dissipation Factor | 1MHz | IEC 60250 | 1.4E-03 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 4 |
| dielectric constant | | ASTM D150/IEC 60250 | 3.90 |
| Physical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792/ISO 1183 | 1.64 |
| Shrinkage rate | | ASTM D955 | 0.3-0.8 % |
| Water absorption rate | | ASTM D570/ISO 62 | 0.02 % |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | | 自定标准 | 2.2 |
| UL flame retardant rating | | UL 94 | V-0 |
| Heat distortion temperature | 1.82MPa，HDT | ASTM D-648 | ＞260 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | >260 °C |
| melting temperature | | 内部方法 | 285 °C |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 260 ℃（℉） |
| melting temperature | | | 285 ℃（℉） |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.