| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183/B | 1.20 g/cm³ |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 22 g/10min |
| Shrinkage rate | MD | ISO 294-4 | 0.50to0.70 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.15 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.32 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M计秤 | ISO 2039-2 | 73 |
| Rockwell hardness | R-Scale | ISO 2039-2 | 118 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Haze ratio | 2000µm | | 92 % |
| Haze ratio | 3000µm | | 96 % |
| Yellowness Index | 1.00mm | ASTM D1925 | 3.0 YI |
| Yellowness Index | 2.00mm | ASTM D1925 | 6.1 YI |
| Yellowness Index | 3.00mm | ASTM D1925 | 8.9 YI |
| Color A | 1.00mm | | 0.0100 |
| Color A | 2.00mm | | 0.140 |
| Color A | 3.00mm | | 0.360 |
| Color B | 1.00mm | | 1.63 |
| Color B | 2.00mm | | 3.14 |
| Color B | 3.00mm | | 4.34 |
| diffusion coefficient | 1.00mm | | 78 |
| diffusion coefficient | 2.00mm | | 68 |
| diffusion coefficient | 3.00mm | | 58 |
| Color L | 1.00mm | | 91.5 |
| transmissivity | 2000µm | | 71.6 % |
| transmissivity | 3000µm | | 62.9 % |
| Haze ratio | 1000µm | | 79 % |
| transmissivity | 1000µm | | 79.6 % |
| Color L | 2.00mm | | 87.8 |
| Color L | 3.00mm | | 83.4 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 800 °C |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 775 °C |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 775 °C |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 900 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 26 % |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 875 °C |
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 875 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2/50 | 2300 MPa |
| tensile strength | Yield | ISO 527-2/50 | 60.0 MPa |
| tensile strength | Break | ISO 527-2/50 | 65.0 MPa |
| Tensile strain | Yield | ISO 527-2/50 | 6.0 % |
| Tensile strain | Break | ISO 527-2/50 | 120 % |
| Flexural modulus | | ISO 178 | 2400 MPa |
| bending strength | | ISO 178 | 97.0 MPa |
| Taber abraser | | ASTM D1044 | 45 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 20 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 74 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | IEC 60093 | >1.0E+13 ohms·cm |
| dielectric strength | | IEC 60243-1 | 17 kV/mm |
| relative permittivity | 100Hz | IEC 60250 | 3.00 |
| relative permittivity | 1MHz | IEC 60250 | 3.00 |
| Dissipation Factor | 50Hz | IEC 60250 | 1E-03 |
| Dissipation Factor | 1MHz | IEC 60250 | 2E-03 |
| Compared to the Leakage Tracking Index (CTI) | 2.00mm,SolutionA | IEC 60112 | PLC 2 |
| dielectric constant | 60Hz | IEC 60250 | 3.00 |
| dielectric constant | 1MHz | IEC 60250 | 3.00 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 139 °C |
| vicat | | ISO 306/B50 | 147 °C |
| Ball pressure temperature | | IEC 60598-1 | >125 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 142 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 122 °C |