Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 303-22 Trinseo
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Trinseo/303-22 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 20 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 74 kJ/m² |
| hardness | Test Condition | Test Method | Trinseo/303-22 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 118 |
| M计秤 | ISO 2039-2 | 73 |
| Electrical performance | Test Condition | Test Method | Trinseo/303-22 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 17 kV/mm | |
| dielectric constant | 60Hz | IEC 60250 | 3.00 |
| Compared to the Leakage Tracking Index (CTI) | 2.00mm,SolutionA | IEC 60112 | PLC 2 |
| Volume resistivity | IEC 60093 | >1.0E+13 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.00 |
| dielectric constant | 1MHz | IEC 60250 | 3.00 |
| relative permittivity | 1MHz | IEC 60250 | 3.00 |
| Dissipation Factor | 50Hz | IEC 60250 | 1E-03 |
| 1MHz | IEC 60250 | 2E-03 |
| Mechanical properties | Test Condition | Test Method | Trinseo/303-22 |
|---|---|---|---|
| Taber abraser | ASTM D1044 | 45 % | |
| Tensile modulus | ISO 527-2/50 | 2300 MPa | |
| Flexural modulus | ISO 178 | 2400 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 120 % |
| 屈服 | ISO 527-2/50 | 6.0 % | |
| tensile strength | 屈服 | ISO 527-2/50 | 60.0 MPa |
| bending strength | ISO 178 | 97.0 MPa | |
| tensile strength | 断裂 | ISO 527-2/50 | 65.0 MPa |
| optical performance | Test Condition | Test Method | Trinseo/303-22 |
|---|---|---|---|
| Yellowness Index | 1.00mm | ASTM D1925 | 3.0 YI |
| transmissivity | 1000µm | 79.6 % | |
| diffusion coefficient | 3.00mm | 58 | |
| Haze ratio | 3000µm | 96 % | |
| Color L | 1.00mm | 91.5 | |
| transmissivity | 2000µm | 71.6 % | |
| Yellowness Index | 2.00mm | ASTM D1925 | 6.1 YI |
| Color B | 1.00mm | 1.63 | |
| 3.00mm | 4.34 | ||
| Color A | 1.00mm | 0.0100 | |
| Color L | 3.00mm | 83.4 | |
| Haze ratio | 1000µm | 79 % | |
| diffusion coefficient | 1.00mm | 78 | |
| transmissivity | 3000µm | 62.9 % | |
| Color A | 3.00mm | 0.360 | |
| diffusion coefficient | 2.00mm | 68 | |
| Haze ratio | 2000µm | 92 % | |
| Color A | 2.00mm | 0.140 | |
| Color L | 2.00mm | 87.8 | |
| Yellowness Index | 3.00mm | ASTM D1925 | 8.9 YI |
| Color B | 2.00mm | 3.14 |
| flammability | Test Condition | Test Method | Trinseo/303-22 |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 875 °C |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 775 °C |
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 775 °C |
| 1.0mm | IEC 60695-2-13 | 800 °C | |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 900 °C |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 26 % | |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 875 °C |
| physical property | Test Condition | Test Method | Trinseo/303-22 |
|---|---|---|---|
| Shrinkage rate | MD | ISO 294-4 | 0.50to0.70 % |
| density | ISO 1183/B | 1.20 g/cm³ | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.15 % |
| 平衡,23°C,50%RH | ISO 62 | 0.32 % | |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 22 g/10min |
| Thermal performance | Test Condition | Test Method | Trinseo/303-22 |
|---|---|---|---|
| Ball pressure temperature | IEC 60598-1 | >125 °C | |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 139 °C |
| vicat | ISO 306/B50 | 147 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 122 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 142 °C |