physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D-792	1.90
	320℃,98MPa,1mm厚，流动长	东丽法	110 ×10
Shrinkage rate	流动方向	东丽法	0.15 %
Shrinkage rate	Shrinkage rate	垂重方向	东丽法	0.55 %

Basic performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Water absorption rate		ASTM D-570	0.02 %

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
bending strength		ASTM D-790	190 Mpa
tensile strength		ASTM D-638	145 Mpa
limiting pv value		东丽法	815 KJ/m
tensile strength		ASTM D-638	1.3 %
coefficient of friction	对钢	ASTM D-1894	0.28
abrasion		ASTM D-1044	70 mg/1000回
bending strength		ASTM D-790	15.1 GPa
elongation at break		ASTM D-732	65
Impact strength of cantilever beam gap	缺口23℃	ASTM D-256	100 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	无缺口23℃	ASTM D-256	25 KJ/m
Shore hardness		ASTM D-785	122 洛氏

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Inherent resistance of volume		ASTM D-257	10 Ω.m
arc resistance	W电极	ASTM D-495	128 秒
Induced positive connection	10	ASTM D-150	0.002
dielectric constant	10	ASTM D-150	5.0
dielectric strength		ASTM D-149	15 MV/m

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
combustibility		UL -94	V-0
Linear coefficient of thermal expansion	流动方向	ASTM D-696	1.7 ×10
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	垂重方向	ASTM D-696	2.5 ×10
melting temperature		DSC	278 °C
Heat distortion temperature	1.82MPa，HDT	ASTM D-648	>260 °C