برگه داده فنی مقایسهoptical performance شرایط آزمون روش آزمون نتیجه آزمون transparency 50.8μm ASTM D1746 70.0 turbidity 50.8μm ASTM D1003 1.3 % gloss 20°,50.8μm ASTM D2457 134
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature ASTM D1525 76.7 °C Melting temperature Internal Method 96.1 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 190°C/2.16kg ASTM D1238 1.6 g/10min
film شرایط آزمون روش آزمون نتیجه آزمون tensile strength TD:Break,51μm ASTM D882 39.5 Mpa elongation MD:Break,51μm ASTM D882 690 % elongation TD:Break,51μm ASTM D882 700 % Dart impact 51μm ASTM D1709B >850 g Elmendorf tear strength MD:51μm ASTM D1922 470 g Elmendorf tear strength TD:51μm ASTM D1922 620 g Initial sealing temperature 51μm Internal Method 81.1 °C film thickness 51 µm Thin film puncture strength 51μm Internal Method 8.18 J Thin film puncture strength 51μm Internal Method 83.6 N Thin film puncture strength 51μm Internal Method 20.3 J/cm³ Secant modulus 2%Secant,MD:51μm ASTM D882 72.8 Mpa Secant modulus 2%Secant,TD:51μm ASTM D882 73.2 Mpa tensile strength MD:Yield,51μm ASTM D882 5.79 Mpa tensile strength TD:Yield,51μm ASTM D882 6.34 Mpa tensile strength MD:Break,51μm ASTM D882 50.3 Mpa
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.