Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POP 1140G STYRON US
AFFINITY™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | STYRON US/1140G |
|---|---|---|---|
| Elmendorf tear strength | TD:51µm | ASTM D1922 | 620 g |
| tensile strength | TD:屈服,51µm | ASTM D882 | 6.34 Mpa |
| Secant modulus | 2%正割,TD:51µm | ASTM D882 | 73.2 Mpa |
| tensile strength | TD:断裂,51µm | ASTM D882 | 39.5 Mpa |
| Dart impact | 51µm | ASTM D1709B | >850 g |
| Thin film puncture strength | 51µm | 内部方法 | 8.18 J |
| elongation | MD:断裂,51µm | ASTM D882 | 690 % |
| tensile strength | MD:屈服,51µm | ASTM D882 | 5.79 Mpa |
| Initial sealing temperature | 51µm | 内部方法 | 81.1 °C |
| Secant modulus | 2%正割,MD:51µm | ASTM D882 | 72.8 Mpa |
| tensile strength | MD:断裂,51µm | ASTM D882 | 50.3 Mpa |
| elongation | TD:断裂,51µm | ASTM D882 | 700 % |
| Thin film puncture strength | 51µm | 内部方法 | 83.6 N |
| film thickness | 51 µm | ||
| Elmendorf tear strength | MD:51µm | ASTM D1922 | 470 g |
| Thin film puncture strength | 51µm | 内部方法 | 20.3 J/cm³ |
| optical performance | Test Condition | Test Method | STYRON US/1140G |
|---|---|---|---|
| gloss | 20°,50.8µm | ASTM D2457 | 134 |
| transparency | 50.8µm | ASTM D1746 | 70.0 |
| Haze ratio | 50.8µm | ASTM D1003 | 1.3 % |
| physical property | Test Condition | Test Method | STYRON US/1140G |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 1.6 g/10min |
| Thermal performance | Test Condition | Test Method | STYRON US/1140G |
|---|---|---|---|
| vicat | ASTM D1525 | 76.7 °C | |
| melting temperature | 内部方法 | 96.1 °C |