برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون Ignition temperature of heating wire 2.0mm IEC 60695-2-13 800 °C Burning wire flammability index 2.0mm IEC 60695-2-12 960 °C UL flame retardant rating 2.5mm UL 94 V-0 UL flame retardant rating 1.6mm UL 94 V-0
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون bending strength 4.00mm,InjectionMolded ISO 178 92.0 Mpa Bending modulus 4.00mm,InjectionMolded ISO 178 2700 Mpa Tensile strain Break,4.00mm,Injection ISO 527-2/50 40 % Tensile strain Yield,4.00mm,InjectionMolded ISO 527-2/50 4.0 % tensile strength Break,4.00mm,Injection ISO 527-2/50 47.0 Mpa tensile strength Yield,4.00mm,InjectionMolded ISO 527-2/50 60.0 Mpa Tensile modulus 4.00mm,Injection ISO 527-2/1 2600 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa,Unannealed ISO 75-2/B 90.0 °C Ball pressure temperature IEC 60335-1 95.0 °C Vicat softening temperature -- ISO 306/B50 98.0 °C Vicat softening temperature -- ISO 306/A120 105 °C Hot deformation temperature 1.8MPa,Unannealed ISO 75-2/A 80.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD ISO 294-4 0.40-0.60 % melt mass-flow rate 260°C/5.0kg ISO 1133 95 g/10min melt mass-flow rate 230°C/3.8kg ISO 1133 20 g/10min Apparent density ISO 60 0.67 g/cm³
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.