Filling analysis	شرایط آزمون	روش آزمون	نتیجه آزمون
melt viscosity	260°C	内部方法	810000 mPa·s
Average Specific Heat Capacity	20 到 150°C		2250 J/kg/°C
Puncture Resistance		内部方法	13.0 J/cm
RSV - Formic Acid, 1g/100ml		内部方法	3.03

squeeze out	شرایط آزمون	روش آزمون	نتیجه آزمون
Temperature in Zone 1 of the material cylinder			270 °C
Temperature in Zone 2 of the material cylinder			270 °C
Temperature in Zone 3 of the material cylinder			270 °C
Temperature in Zone 4 of the material cylinder			270 °C
die temperature			270 °C
pull roll			110 °C

film	شرایط آزمون	روش آزمون	نتیجه آزمون
Film thickness - tested			50 µm
Tensile modulus		内部方法	455 Mpa
Tensile stress	屈服，MD	ISO 527-3	31.0 Mpa
Tensile stress	Tensile stress	断裂，MD	ISO 527-3	82.0 Mpa
elongation	断裂， MD	ISO 527-3	350 %
Trouser Tear - Parallel		ISO 6383-1	32.0
Water Vapor Transmission Rate	23°C, 85% RH	DIS 15106-1/-3	35 g/m²/24 hr
OTr	0% RH : 23°C	ASTM D256A	26 cm³/m²/bar/24 hr
OTr	OTr	85% RH : 23°C	ASTM D256A	38 cm³/m²/bar/24 hr

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Linear coefficient of thermal expansion	流动	ISO 11359-2	9.0E-5 cm/cm/°C
Specific heat capacity			1550 J/kg/°C