برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus ISO 527-2 2500 Mpa tensile strength Yield ISO 527-2 62.0 Mpa tensile strength -- ASTM D638 62.0 Mpa elongation Break ASTMD638 40 % Bending modulus -- ASTM D790 2450 Mpa Bending modulus -- ISO 178 2400 Mpa bending strength ASTM D790 88.0 Mpa Taber abraser ASTM D1044 14.0 mg
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa,Unannealed ASTM D648 158 °C Hot deformation temperature 0.45MPa,Unannealed ISO 75-2/B 156 °C Hot deformation temperature 1.8MPa,Unannealed ASTM D648 110 °C Hot deformation temperature 1.8MPa,Unannealed ISO 75-2/A 95.0 °C Linear coefficient of thermal expansion MD ASTMD696 1E-04 cm/cm/°C specific heat 1470 J/kg/°C thermal conductivity 0.23 W/m/K
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 190°C/2.16kg ISO 1133 2.8 g/10min Shrinkage rate MD Internal Method 1.6-2.0 % Water absorption rate 23°C,24hr,50%RH ASTM D570 0.20 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Volume resistivity 23°C ASTM D257 1.0E+15-1.0E+16 ohms·cm Dielectric strength ASTM D149 19 KV/mm Dielectric constant 23°C,1MHz ASTM D150 3.90 Dissipation factor 23°C,1MHz ASTM D150 8E-03 Arc resistance ASTM D495 250 sec Surface resistivity ASTM D257 1.0E+16-1.0E+17 ohms
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness M-Scale ASTM D785 78