physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	TD:23°C,2.00mm	ISO 294-4	0.90 %
Shrinkage rate	Shrinkage rate	MD:23°C,2.00mm	ISO 294-4	0.40 %
Water absorption rate	23°C,24hr	ISO 62	0.90 %
Water absorption rate	Water absorption rate	平衡,50%RH	ISO 62	1.9 %

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of simply supported beam without notch	-30°C	ISO 179	87 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	95 kJ/m²

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus	23°C	ISO 527-2	9650 Mpa
tensile strength	断裂,23°C	ISO 527-2	185 Mpa
Tensile strain	断裂,23°C	ISO 527-2	4.0 %
Flexural modulus	23°C	ISO 178	9000 Mpa
bending strength	23°C	ISO 178	270 Mpa
Poisson's Ratio	23°C	ISO 527	0.40

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa,未退火，HDT	ISO 75-2/B	258 °C
Heat distortion temperature	Heat distortion temperature	1.8MPa,未退火，HDT	ISO 75-2/A	247 °C
melting temperature		ISO 11357-3	260 °C
Linear coefficient of thermal expansion	MD：23to55°C,2.00mm	ISO 11359-2	2.2E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C,2.00mm	ISO 11359-2	1.1E-04 cm/cm/°C