Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 R530HR BK652 ASCEND USA
Vydyne®
Automotive components
Chemical resistance,Fatigue resistance,High mobility,Solvent resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASCEND USA/R530HR BK652 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 87 kJ/m² |
| 23°C | ISO 179 | 95 kJ/m² |
| Mechanical properties | Test Condition | Test Method | ASCEND USA/R530HR BK652 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 4.0 % |
| bending strength | 23°C | ISO 178 | 270 Mpa |
| Poisson's Ratio | 23°C | ISO 527 | 0.40 |
| Flexural modulus | 23°C | ISO 178 | 9000 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 9650 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 185 Mpa |
| physical property | Test Condition | Test Method | ASCEND USA/R530HR BK652 |
|---|---|---|---|
| Shrinkage rate | MD:23°C,2.00mm | ISO 294-4 | 0.40 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.90 % |
| 平衡,50%RH | ISO 62 | 1.9 % | |
| Shrinkage rate | TD:23°C,2.00mm | ISO 294-4 | 0.90 % |
| Thermal performance | Test Condition | Test Method | ASCEND USA/R530HR BK652 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 260 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 258 °C |
| Linear coefficient of thermal expansion | TD：23to55°C,2.00mm | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 247 °C |
| Linear coefficient of thermal expansion | MD：23to55°C,2.00mm | ISO 11359-2 | 2.2E-05 cm/cm/°C |