برگه داده فنی impact performance شرایط آزمون روش آزمون نتیجه آزمون Dart impact -30°C, Energy at Peak ASTM D3763 25.0 J  Dart impact 23°C, Energy at Peak ASTM D3763 53.0 J  
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield ASTM D638 53.0 Mpa  elongation Break ASTM D638 50 %  Bending modulus 100 mm Span ASTM D790 2300 Mpa  bending strength Yield, 100 mm Span ASTM D790 81.0 Mpa  
injection شرایط آزمون روش آزمون نتیجه آزمون drying temperature 95 to 105 °C  drying time 3.0 to 4.0 hr  Suggested maximum moisture content 0.020 %  Suggested injection volume 30 to 70 %  Temperature at the rear of the barrel 230 to 280 °C  Temperature in the middle of the barrel 245 to 290 °C  Temperature at the front of the material cylinder 255 to 295 °C  Spray nozzle temperature 265 to 295 °C  Processing (melt) temperature 265 to 295 °C  Mold temperature 65 to 95 °C  Back pressure 0.300 to 0.700 Mpa  Screw speed 20 to 100 rpm  Exhaust hole depth 0.038 to 0.051 mm  
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45 MPa, Unannealed, 6.40 mm ASTM D648 123 °C  Hot deformation temperature 1.8 MPa, Unannealed, 6.40 mm ASTM D648 121 °C  Linear coefficient of thermal expansion 0 to 100°C,Flow ASTM E831 9.4E-5 cm/cm/°C  
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate 3.20 mm,Flow Internal Method 0.50 - 0.70 %  Water absorption rate 24 hr ASTM D570 0.20 %  