PPO EM6101-8846 SABIC INNOVATIVE US
NORYL™
electromagnetic shielding
Conductive、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/EM6101-8846 |
|---|---|---|---|
| Dart impact | -30°C, Energy at Peak | ASTM D3763 | 25.0 J |
| 23°C, Energy at Peak | ASTM D3763 | 53.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/EM6101-8846 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 50 % |
| bending strength | 屈服, 100 mm 跨距 | ASTM D790 | 81.0 Mpa |
| tensile strength | 屈服 | ASTM D638 | 53.0 Mpa |
| Flexural modulus | 100 mm 跨距 | ASTM D790 | 2300 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/EM6101-8846 |
|---|---|---|---|
| Water absorption rate | 24 hr | ASTM D570 | 0.20 % |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/EM6101-8846 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 0 到 100°C，流动 | ASTM E831 | 9.4E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 121 °C |
| 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 123 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/EM6101-8846 |
|---|---|---|---|
| screw speed | 20 to 100 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 265 to 295 °C | ||
| drying temperature | 95 to 105 °C | ||
| Suggested injection volume | 30 to 70 % | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 245 to 290 °C | ||
| Temperature at the rear of the barrel | 230 to 280 °C | ||
| Exhaust hole depth | 0.038 to 0.051 mm | ||
| Temperature at the front of the material cylinder | 255 to 295 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 65 to 95 °C | ||
| Spray nozzle temperature | 265 to 295 °C |