physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	14 g/10 min
Melt volume flow rate	300°C/1.2 kg	ISO 1133	13.0 cm3/10min
Shrinkage rate	流动 : 3.20 mm	内部方法	0.40 - 0.80 %
Shrinkage rate	Shrinkage rate	横向流动 : 3.20 mm	内部方法	0.40 - 0.80 %
Water absorption rate	平衡, 23°C, 50% RH	ISO 62	0.10 %

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ASTM D638	2300 Mpa
tensile strength	屈服	ASTM D638	58.0 Mpa
tensile strength	tensile strength	断裂	ASTM D638	57.0 Mpa
elongation	屈服	ASTM D638	5.0 %
elongation	elongation	断裂	ASTM D638	85 %
Flexural modulus	50.0 mm 跨距	ASTM D790	2100 Mpa
bending strength	屈服, 50.0 mm 跨距	ASTM D790	85.0 Mpa

injection	شرایط آزمون	روش آزمون	نتیجه آزمون
drying temperature			120 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 60 %
Temperature at the rear of the barrel			270 to 295 °C
Temperature in the middle of the barrel			280 to 305 °C
Temperature at the front of the material cylinder			295 to 315 °C
Spray nozzle temperature			290 to 310 °C
Processing (melt) temperature			295 to 315 °C
Temperature			70 to 95 °C
Back pressure			0.300 to 0.700 Mpa
screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	1.8 MPa, 未退火, 3.20 mm，HDT	ASTM D648	118 °C

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.