Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC ML0992-BK1A068 SABIC INNOVATIVE NANSHA
LEXAN™ 
--
Middle flow,Low temperature and high ,Short molding cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/ML0992-BK1A068
Tensile modulusASTM D6382300 Mpa
elongation断裂ASTM D63885 %
屈服ASTM D6385.0 %
bending strength屈服, 50.0 mm 跨距ASTM D79085.0 Mpa
tensile strength 断裂ASTM D63857.0 Mpa
屈服ASTM D63858.0 Mpa
Flexural modulus50.0 mm 跨距ASTM D7902100 Mpa
physical property Test ConditionTest MethodSABIC INNOVATIVE NANSHA/ML0992-BK1A068
Water absorption rate平衡, 23°C, 50% RHISO 620.10 %
Shrinkage rate横向流动 : 3.20 mm内部方法0.40 - 0.80 %
Melt volume flow rate300°C/1.2 kgISO 113313.0 cm3/10min
melt mass-flow rate300°C/1.2 kgASTM D123814 g/10 min
Shrinkage rate流动 : 3.20 mm内部方法0.40 - 0.80 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/ML0992-BK1A068
Heat distortion temperature1.8 MPa, 未退火, 3.20 mm，HDTASTM D648118 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE NANSHA/ML0992-BK1A068
screw speed40 to 70 rpm
Suggested maximum moisture content0.020 %
Processing (melt) temperature295 to 315 °C
drying temperature120 °C
Suggested injection volume40 to 60 %
drying time3.0 to 4.0 hr
Temperature in the middle of the barrel280 to 305 °C
Temperature at the rear of the barrel270 to 295 °C
Exhaust hole depth0.025 to 0.076 mm
Temperature at the front of the material cylinder295 to 315 °C
Back pressure0.300 to 0.700 Mpa
Temperature70 to 95 °C
Spray nozzle temperature290 to 310 °C