برگه داده فنی مقایسهoptical performance شرایط آزمون روش آزمون نتیجه آزمون gloss 45° ASTM D2457 33 turbidity ASTM D1003 20 %
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature ASTM D1525 106 °C Melting temperature Internal Method 123 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 190°C/2.16kg ASTM D1238 0.85 g/10min
film شرایط آزمون روش آزمون نتیجه آزمون tensile strength TD:Yield ASTM D882 12.4 Mpa tensile strength MD:Break ASTM D882 43.6 Mpa tensile strength TD:Break ASTM D882 36.0 Mpa elongation MD:Break ASTM D882 480 % elongation TD:Break ASTM D882 620 % Dart impact ASTM D1709A 540 g Elmendorf tear strength MD ASTM D1922 260 g Elmendorf tear strength TD ASTM D1922 670 g film thickness 25 µm Thin film puncture strength Internal Method 5.76 J Thin film puncture strength Internal Method 64.5 N Thin film puncture strength Internal Method 28.3 J/cm³ Membrane strength MD ASTM D882 98.5 J/cm³ Membrane strength TD ASTM D882 98.5 J/cm³ Secant modulus 1%Secant,MD ASTM D882 272 Mpa Secant modulus 2%Secant,MD ASTM D882 231 Mpa Secant modulus 1%Secant,TD ASTM D882 309 Mpa Secant modulus 2%Secant,TD ASTM D882 256 Mpa tensile strength MD:Yield ASTM D882 11.9 Mpa
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.