Impact strength of simply supported beam without notch
23°C
ISO 179
45 kJ/m²
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
0.8mm
UL 94
V-0
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
tensile strength
Break
ISO 527-2
135 Mpa
bending strength
ISO 178
210 Mpa
Tensile modulus
ISO 527-2
11000 Mpa
Tensile strain
Break
ISO 527-2
2.0 %
Bending modulus
ISO 178
10500 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
208 °C
Linear coefficient of thermal expansion
TD:50to120°C
ISO 11359-2
1.4E-04 cm/cm/°C
Melting temperature
ISO 11357-3
224 °C
Linear coefficient of thermal expansion
TD:-30to50°C
ISO 11359-2
7E-05 cm/cm/°C
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
>220 °C
Linear coefficient of thermal expansion
MD:50to120°C
ISO 11359-2
2E-05 cm/cm/°C
Linear coefficient of thermal expansion
MD:-30to50°C
ISO 11359-2
2E-05 cm/cm/°C
Linear coefficient of thermal expansion
MD:-30to120°C
ISO 11359-2
2E-05 cm/cm/°C
Linear coefficient of thermal expansion
TD:-30to120°C
ISO 11359-2
1.1E-04 cm/cm/°C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shrinkage rate
MD:2.00mm
0.40 %
Shrinkage rate
吸水率(Saturation,23°C)
0.070 %
Shrinkage rate
TD:2.00mm
1.1 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Dielectric strength
1.00mm
IEC 60243-1
24 KV/mm
Volume resistivity
IEC 60093
5E+16 ohms·cm
Relative permittivity
1MHz
IEC 60250
3.90
Compared to the anti leakage trace index
CTI
UL 746
PLC 3
Surface resistivity
IEC 60093
6E+15 ohms
Dissipation factor
1MHz
IEC 60250
0.014