Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ISO 527-2/1A/1	10500 Mpa
tensile strength	断裂	ISO 527-2/1A/5	175 Mpa
Tensile strain	断裂	ISO 527-2/1A/5	3.2 %
Flexural modulus		ISO 178	10000 Mpa
bending strength	3.7% 应变	ISO 178	280 Mpa
bending strength	bending strength	3.5% 应变	ISO 178	280 Mpa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	65 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80 kJ/m²

injection	شرایط آزمون	روش آزمون	نتیجه آزمون
drying temperature			80 °C
drying time			3.0 to 6.0 hr
Suggested maximum moisture content			0.040 to 0.10 %
Suggested maximum material return ratio			20 %
Processing (melt) temperature			240 to 280 °C
Temperature			50 to 90 °C

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45 MPa, 未退火，HDT	ISO 75-2/Bf	215 °C
Heat distortion temperature	Heat distortion temperature	1.8 MPa, 未退火，HDT	ISO 75-2/Af	195 °C