thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat Deflection Temperature	0.45MPa,未退火,3.20mm，HDT	ASTM D648	142 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,未退火,3.20mm，HDT	ASTM D648	129 °C
vicat		ISO 306/B120	145 °C
Linear coefficient of thermal expansion	MD:-40到95°C	ASTME831	6.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40到95°C	ASTME831	6.4E-05 cm/cm/°C

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
transmissivity	2540µm	ASTM D1003	>90.0 %

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ASTM D638	2220 Mpa
tensile strength	屈服	ASTM D638	60.0 Mpa
tensile strength	tensile strength	断裂	ASTM D638	68.0 Mpa
elongation	屈服	ASTM D638	7.0 %
elongation	elongation	断裂	ASTM D638	140 %
flexural modulus	50.0mm跨距	ASTM D790	2360 Mpa
bending strength	屈服,50.0mm跨距	ASTM D790	96.0 Mpa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Suspended wall beam without notch impact strength	23°C	ASTM D4812	2100 J/m
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	72.0 J

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate	300°C/1.2kg	ASTM D1238	19 g/10min
shrinkage rate	MD1	内部方法	0.60-0.90 %