Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LUX2110T-11024 SABIC INNOVATIVE US
LEXAN™
Plastic bag,Lighting applications
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/LUX2110T-11024 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 2100 J/m |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 72.0 J |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/LUX2110T-11024 |
|---|---|---|---|
| vicat | ISO 306/B120 | 145 °C | |
| Linear coefficient of thermal expansion | TD:-40到95°C | ASTME831 | 6.4E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 142 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 129 °C | |
| Linear coefficient of thermal expansion | MD:-40到95°C | ASTME831 | 6.5E-05 cm/cm/°C |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/LUX2110T-11024 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2220 Mpa | |
| elongation | 断裂 | ASTM D638 | 140 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 96.0 Mpa |
| tensile strength | 屈服 | ASTM D638 | 60.0 Mpa |
| elongation | 屈服 | ASTM D638 | 7.0 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2360 Mpa |
| tensile strength | 断裂 | ASTM D638 | 68.0 Mpa |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/LUX2110T-11024 |
|---|---|---|---|
| transmissivity | 2540µm | ASTM D1003 | >90.0 % |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/LUX2110T-11024 |
|---|---|---|---|
| shrinkage rate | MD1 | 内部方法 | 0.60-0.90 % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 19 g/10min |