برگه داده فنی مقایسهelastomer شرایط آزمون روش آزمون نتیجه آزمون tear strength ASTM D624 142 kN/m
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون bending strength 23°C, 6.40 mm, Injection ASTM D790 12.7 Mpa Bending modulus 23°C, 6.40 mm, Injection ASTM D790 294 Mpa elongation Break, 23°C, 2.00 mm, Injection ASTM D638 550 % tensile strength Break, 23°C, 2.00 mm, Injection ASTM D638 32.4 Mpa
injection شرایط آزمون روش آزمون نتیجه آزمون Mold temperature 40 to 60 °C Processing (melt) temperature 220 to 250 °C Spray nozzle temperature 230 to 250 °C Temperature at the front of the material cylinder 230 to 250 °C Temperature in the middle of the barrel 225 to 245 °C Temperature at the rear of the barrel 220 to 240 °C Suggested maximum moisture content 0.010 % drying time 3.0 to 4.0 hr drying temperature 80 to 90 °C
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Melting temperature ASTM D3418 220 °C Hot deformation temperature 0.45 MPa, Unannealed, 6.40 mm ASTM D648 60.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate 24 hr, 23°C ASTM D570 0.60 % Shrinkage rate 23°C, 3.20 mm, Injection,Flow ASTM D955 1.5 - 1.7 % melt mass-flow rate 240°C/2.16 kg ASTM D1238 15 g/10 min
hardness شرایط آزمون روش آزمون نتیجه آزمون Shore hardness Shore D ASTM D2240 52