Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPEE S-5035 LG CHEM KOREA
KEYFLEX®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | LG CHEM KOREA/S-5035 |
|---|---|---|---|
| Shore hardness | 邵氏 D | ASTM D2240 | 52 |
| Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/S-5035 |
|---|---|---|---|
| Flexural modulus | 23°C, 6.40 mm, 注塑 | ASTM D790 | 294 Mpa |
| tensile strength | 断裂, 23°C, 2.00 mm, 注塑 | ASTM D638 | 32.4 Mpa |
| bending strength | 23°C, 6.40 mm, 注塑 | ASTM D790 | 12.7 Mpa |
| elongation | 断裂, 23°C, 2.00 mm, 注塑 | ASTM D638 | 550 % |
| physical property | Test Condition | Test Method | LG CHEM KOREA/S-5035 |
|---|---|---|---|
| Water absorption rate | 24 hr, 23°C | ASTM D570 | 0.60 % |
| Shrinkage rate | 23°C, 3.20 mm, 注塑，Flow | ASTM D955 | 1.5 - 1.7 % |
| melt mass-flow rate | 240°C/2.16 kg | ASTM D1238 | 15 g/10 min |
| elastomer | Test Condition | Test Method | LG CHEM KOREA/S-5035 |
|---|---|---|---|
| tear strength | ASTM D624 | 142 kN/m |
| Thermal performance | Test Condition | Test Method | LG CHEM KOREA/S-5035 |
|---|---|---|---|
| melting temperature | ASTM D3418 | 220 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 60.0 °C |
| injection | Test Condition | Test Method | LG CHEM KOREA/S-5035 |
|---|---|---|---|
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.010 % | ||
| Temperature in the middle of the barrel | 225 to 245 °C | ||
| Temperature at the rear of the barrel | 220 to 240 °C | ||
| Processing (melt) temperature | 220 to 250 °C | ||
| drying temperature | 80 to 90 °C | ||
| Temperature at the front of the material cylinder | 230 to 250 °C | ||
| Temperature | 40 to 60 °C | ||
| Spray nozzle temperature | 230 to 250 °C |