Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ASTM D638	2480 Mpa
tensile strength	屈服	ASTM D638	63.0 Mpa
tensile strength	tensile strength	断裂	ASTM D638	42.0 Mpa
elongation	屈服	ASTM D638	4.0 %
elongation	elongation	断裂	ASTM D638	65 %
Flexural modulus	50.0 mm 跨距	ASTM D790	2240 Mpa
bending strength	屈服, 50.0 mm 跨距	ASTM D790	89.0 Mpa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Dart impact	23°C, Total Energy	ASTM D3763	65.0 J

injection	شرایط آزمون	روش آزمون	نتیجه آزمون
drying temperature			80 to 90 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.040 %
Suggested injection volume			30 to 80 %
Temperature at the rear of the barrel			220 to 255 °C
Temperature in the middle of the barrel			220 to 265 °C
Temperature at the front of the material cylinder			245 to 275 °C
Spray nozzle temperature			245 to 275 °C
Processing (melt) temperature			245 to 275 °C
Temperature			60 to 80 °C
Back pressure			0.300 to 0.700 Mpa
screw speed			40 to 70 rpm
Exhaust hole depth			0.038 to 0.076 mm

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	1.8 MPa, 未退火, 3.20 mm，HDT	ASTM D648	78.0 °C
vicat		ASTM D15255	102 °C