Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT ENH2900-BK1066 SABIC INNOVATIVE US
XENOY™
Household daily necessiti、Electrical applications、Automotive Applications
Chemical resistance、Low temperature impact re
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/ENH2900-BK1066 |
|---|---|---|---|
| Dart impact | 23°C, Total Energy | ASTM D3763 | 65.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/ENH2900-BK1066 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2480 Mpa | |
| elongation | 断裂 | ASTM D638 | 65 % |
| 屈服 | ASTM D638 | 4.0 % | |
| bending strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 89.0 Mpa |
| tensile strength | 断裂 | ASTM D638 | 42.0 Mpa |
| 屈服 | ASTM D638 | 63.0 Mpa | |
| Flexural modulus | 50.0 mm 跨距 | ASTM D790 | 2240 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/ENH2900-BK1066 |
|---|---|---|---|
| UL flame retardant rating | 2.5 mm | UL 94 | 5VB |
| 1.1 mm | UL 94 | V-1 | |
| 1.5 mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/ENH2900-BK1066 |
|---|---|---|---|
| melt mass-flow rate | 266°C/5.0 kg | ASTM D1238 | 26 g/10 min |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.80 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/ENH2900-BK1066 |
|---|---|---|---|
| vicat | ASTM D15255 | 102 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 78.0 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/ENH2900-BK1066 |
|---|---|---|---|
| screw speed | 40 to 70 rpm | ||
| Suggested maximum moisture content | 0.040 % | ||
| Processing (melt) temperature | 245 to 275 °C | ||
| drying temperature | 80 to 90 °C | ||
| Suggested injection volume | 30 to 80 % | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 220 to 265 °C | ||
| Temperature at the rear of the barrel | 220 to 255 °C | ||
| Exhaust hole depth | 0.038 to 0.076 mm | ||
| Temperature at the front of the material cylinder | 245 to 275 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 60 to 80 °C | ||
| Spray nozzle temperature | 245 to 275 °C |