برگه داده فنی مقایسهOther performance شرایط آزمون روش آزمون نتیجه آزمون Spiral flow length 2 seconds injection,25℃ Internal Method 635 mm
Basic Performance شرایط آزمون روش آزمون نتیجه آزمون density ASTM D-792 0.953 Mpa melt mass-flow rate 190℃/2.16kg ISO 1133 4 g/10min melt mass-flow rate 190℃/5.0kg ISO 1133 12 g/10min
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Environmental stress cracking resistance 50℃,100% Antarox,Compression Molded ASTM D-1693 10 hr tensile strength Yield,Compression Molded ASTM D-638 25 Mpa tensile strength Compression Molded,Break ASTM D-638 27 Mpa Elongation at Break Compression Molded ASTM D-638 > 1600 % Bending modulus Compression Molded ASTM D-790 850 Mpa Impact strength of cantilever beam gap Compression Molded ASTM D-1822 85 KJ/m Shore hardness Shore D,Compression Molded ISO 868 65
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature ISO 306/A 128 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate 250℃ ASTM D-955 2.6 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.