thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
melting temperature		ISO 11357-1	225 °C
Glass Transition Temperature		ISO 11357-1	60 °C
Heat Deflection Temperature	1.8Mpa，HDT	ISO 75-1/-2	50 °C
Heat Deflection Temperature	Heat Deflection Temperature	0.45Mpa，HDT	ISO 75-1/-2	150 °C
vicat		ISO 306	185 °C
Linear coefficient of thermal expansion	纵向	ISO 11359-2	1.3 E-4/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向	ISO 11359-2	0.88 E-4/℃

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus	1mm/min	ISO 527-2/1A	2600 Mpa
Tensile stress	50mm/min，屈服	ISO 527-2/1A	60 Mpa
Tensile modulus	50mm/min，屈服	ISO 527-2/1A	6 %
Elongation at break	50mm/min	ISO 527-2/1A	200 %
flexural modulus	23℃	ISO 178	2500 Mpa
bending strength	23℃	ISO 178	80 Mpa
Charpy Notched Impact Strength	23℃	ISO 179/1eU	NB KJ/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23℃	ISO 179/1eA	7.0 KJ/m
Impact strength of cantilever beam gap	23℃	ISO 180/1A	5.5 KJ/m
Rockwell hardness		ISO 2039-2	72 M

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
volume resistivity		IEC 60093	＞1E13 ohm.m
Surface Resistivity		IEC 60093	＞1E15 Ohm
Compared to the Leakage Traceability Index (CTI)		IEC 60112	600
volume resistivity	100Hz	IEC 60250	4
volume resistivity	volume resistivity	1MHz	IEC 60250	3.2
Dielectric dissipation factor	1MHz	IEC 60250	200 E-4

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ISO 1183	1310 kg/m
shrinkage rate		ISO 294-4	1.8-2.0 %
Water absorption rate	23℃,饱和	ISO 62	0.45 %