Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 2001 CELANESE USA
CELANEX®
Electronic and electrical accessories,Automotive sector
Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | CELANESE USA/2001 |
|---|---|---|---|
| Volume resistivity | 1MHz | IEC 60250 | 3.2 |
| Dielectric dissipation factor | 1MHz | IEC 60250 | 200 E-4 |
| Surface Resistivity | IEC 60093 | ＞1E15 Ohm | |
| Volume resistivity | 100Hz | IEC 60250 | 4 |
| IEC 60093 | ＞1E13 ohm.m | ||
| Compared to the Leakage Traceability Index (CTI) | IEC 60112 | 600 |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/2001 |
|---|---|---|---|
| Flexural modulus | 23℃ | ISO 178 | 2500 Mpa |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 5.5 KJ/m |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 7.0 KJ/m |
| elongation at break | 50mm/min | ISO 527-2/1A | 200 % |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eU | NB KJ/m |
| Tensile modulus | 1mm/min | ISO 527-2/1A | 2600 Mpa |
| Tensile stress | 50mm/min，屈服 | ISO 527-2/1A | 60 Mpa |
| Tensile modulus | 50mm/min，屈服 | ISO 527-2/1A | 6 % |
| Rockwell hardness | ISO 2039-2 | 72 M | |
| bending strength | 23℃ | ISO 178 | 80 Mpa |
| physical property | Test Condition | Test Method | CELANESE USA/2001 |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 1.8-2.0 % | |
| Water absorption rate | 23℃,饱和 | ISO 62 | 0.45 % |
| density | ISO 1183 | 1310 kg/m |
| Thermal performance | Test Condition | Test Method | CELANESE USA/2001 |
|---|---|---|---|
| Glass Transition Temperature | ISO 11357-1 | 60 °C | |
| Heat distortion temperature | 1.8Mpa，HDT | ISO 75-1/-2 | 50 °C |
| 0.45Mpa，HDT | ISO 75-1/-2 | 150 °C | |
| vicat | ISO 306 | 185 °C | |
| melting temperature | ISO 11357-1 | 225 °C | |
| Linear coefficient of thermal expansion | 横向 | ISO 11359-2 | 0.88 E-4/℃ |
| 纵向 | ISO 11359-2 | 1.3 E-4/℃ |