برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 0.8 mm UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Break, 3.20 mm ASTM D638 25.0 Mpa elongation Break, 3.20 mm ASTM D638 860 % Bending modulus 3.20 mm ASTM D790 49.0 Mpa bending strength 3.20 mm ASTM D790 4.00 Mpa
injection شرایط آزمون روش آزمون نتیجه آزمون drying temperature 100 to 110 °C drying time 3.0 to 8.0 hr Suggested maximum moisture content < 0.10 % Temperature at the rear of the barrel 180 to 190 °C Temperature in the middle of the barrel 200 to 220 °C Temperature at the front of the material cylinder 210 to 220 °C Spray nozzle temperature 210 to 220 °C Mold temperature 20 to 40 °C
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature ASTM D15253 138 °C Melting temperature ASTM D3418 195 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 230°C/2.16 kg ASTM D1238 12 g/10 min Shrinkage rate Flow ASTM D955 1.1 % Water absorption rate 24 hr, 23°C ASTM D570 0.70 %
hardness شرایط آزمون روش آزمون نتیجه آزمون Shore hardness Shore D ASTM D2240 39