Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
270 kJ/m²
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
FMVSS flammability
FMVSS302
B
Burning rate
1.00mm
ISO 3795
<100 mm/min
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
bending strength
3.5%Strain
ISO 178
75.0 Mpa
Bending modulus
ISO 178
2900 Mpa
Nominal tensile fracture strain
ISO 527-2
40 %
Tensile strain
Yield
ISO 527-2
21 %
tensile strength
Yield
ISO 527-2
66.0 Mpa
Tensile modulus
ISO 527-2
3000 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Linear coefficient of thermal expansion
TD:-40to23°C
ISO 11359-2
1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion
TD:--
ISO 11359-2
1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion
MD:-40to23°C
ISO 11359-2
1E-04 cm/cm/°C
Linear coefficient of thermal expansion
MD:--
ISO 11359-2
1E-04 cm/cm/°C
Melting temperature
ISO 11357-3
176 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
96.0 °C
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
158 °C