Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM 500SC NC010 DUPONT USA
Delrin®
Engine parts,Fitness equipment
lubrication
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/500SC NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 270 kJ/m² |
| thermal performance | Test Condition | Test Method | DUPONT USA/500SC NC010 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 96.0 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 158 °C | |
| Linear coefficient of thermal expansion | TD：-40to23°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| MD：-- | ISO 11359-2 | 1E-04 cm/cm/°C | |
| MD：-40to23°C | ISO 11359-2 | 1E-04 cm/cm/°C | |
| TD：-- | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
| melting temperature | ISO 11357-3 | 176 °C |
| mechanical properties | Test Condition | Test Method | DUPONT USA/500SC NC010 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2 | 40 % | |
| bending strength | 3.5%应变 | ISO 178 | 75.0 Mpa |
| Tensile modulus | ISO 527-2 | 3000 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 66.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 21 % |
| flexural modulus | ISO 178 | 2900 Mpa |
| flammability | Test Condition | Test Method | DUPONT USA/500SC NC010 |
|---|---|---|---|
| FMVSS flammability | FMVSS302 | B | |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |