برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.6 mm UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون bending strength 23°C, 6.40 mm, Injection ASTM D790 177 Mpa Bending modulus 23°C, 6.40 mm, Injection ASTM D790 8240 Mpa elongation Break, 23°C, 3.20 mm, Injection ASTM D638 2.0 % tensile strength Break, 23°C, 3.20 mm, Injection ASTM D638 123 Mpa
injection شرایط آزمون روش آزمون نتیجه آزمون Mold temperature 40 to 80 °C Processing (melt) temperature 240 to 260 °C Spray nozzle temperature 245 to 265 °C Temperature at the front of the material cylinder 245 to 265 °C Temperature in the middle of the barrel 240 to 260 °C Temperature at the rear of the barrel 240 to 260 °C Suggested maximum moisture content 0.020 % drying time 4.0 to 6.0 hr drying temperature 120 °C
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Melting temperature ASTM D3418 223 °C Hot deformation temperature 1.8 MPa, Unannealed, 6.40 mm, Injection ASTM D648 195 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate 24 hr, 23°C ASTM D570 0.060 % Shrinkage rate 23°C, Injection,Flow ASTM D955 0.30 - 0.50 % melt mass-flow rate 250°C/2.16 kg ASTM D1238 13 g/10 min
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.