برگه داده فنی مقایسهoptical performance شرایط آزمون روش آزمون نتیجه آزمون gloss 20°,50.8μm ASTM D2457 128 transparency 50.8μm ASTM D1746 63.0 turbidity 50.8μm ASTM D1003 2.5 %
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature ASTM D1525 95.0 °C Melting temperature Internal Method 106 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 190°C/2.16kg ASTM D1238 1.0 g/10min
film شرایط آزمون روش آزمون نتیجه آزمون film thickness 51 µm Thin film puncture strength 51μm Internal Method 9.16 J Thin film puncture strength 51μm Internal Method 93.0 N Thin film puncture strength 51μm Internal Method 25.2 J/cm³ Secant modulus 2%Secant,MD:51μm ASTM D882 123 Mpa Secant modulus 2%Secant,TD:51μm ASTM D882 123 Mpa tensile strength MD:Yield,51μm ASTM D882 8.76 Mpa tensile strength TD:Yield,51μm ASTM D882 8.07 Mpa tensile strength MD:Break,51μm ASTM D882 47.8 Mpa tensile strength TD:Break,51μm ASTM D882 45.4 Mpa elongation MD:Break,51μm ASTM D882 620 % elongation TD:Break,51μm ASTM D882 580 % Dart impact 51μm ASTM D1709B >830 g Elmendorf tear strength MD:51μm ASTM D1922 560 g Elmendorf tear strength TD:51μm ASTM D1922 840 g Initial sealing temperature 51μm Internal Method 92.8 °C
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.