Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POP 1840G STYRON US
AFFINITY™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | STYRON US/1840G |
|---|---|---|---|
| tensile strength | TD:屈服,51µm | ASTM D882 | 8.07 Mpa |
| Elmendorf tear strength | TD:51µm | ASTM D1922 | 840 g |
| Secant modulus | 2%正割,TD:51µm | ASTM D882 | 123 Mpa |
| tensile strength | TD:断裂,51µm | ASTM D882 | 45.4 Mpa |
| Dart impact | 51µm | ASTM D1709B | >830 g |
| Thin film puncture strength | 51µm | 内部方法 | 9.16 J |
| tensile strength | MD:屈服,51µm | ASTM D882 | 8.76 Mpa |
| elongation | MD:断裂,51µm | ASTM D882 | 620 % |
| Initial sealing temperature | 51µm | 内部方法 | 92.8 °C |
| Secant modulus | 2%正割,MD:51µm | ASTM D882 | 123 Mpa |
| tensile strength | MD:断裂,51µm | ASTM D882 | 47.8 Mpa |
| elongation | TD:断裂,51µm | ASTM D882 | 580 % |
| Thin film puncture strength | 51µm | 内部方法 | 93.0 N |
| film thickness | 51 µm | ||
| Thin film puncture strength | 51µm | 内部方法 | 25.2 J/cm³ |
| Elmendorf tear strength | MD:51µm | ASTM D1922 | 560 g |
| optical performance | Test Condition | Test Method | STYRON US/1840G |
|---|---|---|---|
| gloss | 20°,50.8µm | ASTM D2457 | 128 |
| transparency | 50.8µm | ASTM D1746 | 63.0 |
| Haze ratio | 50.8µm | ASTM D1003 | 2.5 % |
| physical property | Test Condition | Test Method | STYRON US/1840G |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 1.0 g/10min |
| Thermal performance | Test Condition | Test Method | STYRON US/1840G |
|---|---|---|---|
| vicat | ASTM D1525 | 95.0 °C | |
| melting temperature | 内部方法 | 106 °C |