برگه داده فنی مقایسهBasic Performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 220℃,10kg JIS K-6874 10 g/10min
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap ASTM D256/ISO 179 78 kg·cm/cm(J/M)ft·lb/in tensile strength ASTM D638/ISO 527 42 kg/cm²(MPa)[Lb/in²] Rockwell hardness ASTM D785 114 Bending modulus ASTM D790/ISO 178 2350 kg/cm²(MPa)[Lb/in²] bending strength ASTM D790/ISO 178 74 kg/cm²(MPa)[Lb/in²] Impact strength of cantilever beam gap ASTM D256/ISO 179 206 kg·cm/cm(J/M)ft·lb/in bending strength 15mm/min ASTM D-790 74 Mpa Rockwell hardness 23℃ ASTM D-785 114 R tensile strength ASTM D-638 42 Mpa Impact strength of cantilever beam gap 1/4"带Notched23℃ ASTM D-256 206 J/m Bending modulus 15mm/min ASTM D-790 2350 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature HDT ASTM D648/ISO 75 100 ℃(℉) Vicat softening temperature ASTM D1525/ISO R306 110 ℃(℉) Vicat softening temperature 5kg JIS K-7206 110 °C Hot deformation temperature 6.4mm,1.82MPa ASTM D-648 100 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792/ISO 1183 1.05 Shrinkage rate ASTM D955 0.4-0.6 % melt mass-flow rate ASTM D1238/ISO 1133 10 g/10min
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.