Impact strength of simply supported beam without notch
-30℃-30°C
ISO 179/1eU
90 kJ/m²
Impact strength of simply supported beam without notch
23℃23°C
ISO 179/1eU
90 kJ/m²
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shore hardness
Shore D,15 SecShore D,15 Sec
ISO 868
--
Ball Pressure Test
ISO 2039-1
-- Mpa
Tensile modulus
ISO 527-2
12000 Mpa
tensile strength
BreakBreak
ISO 527-2
155 Mpa
Tensile stress
BreakBreak
ISO 527-2
5 %
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Continuous use temperature
---- 33
ISO 2578
90.0 to 120 °C
Continuous use temperature
---- 44
Internal Method
150 °C
Melting temperature
ISO 11357-3
178 °C
Linear coefficient of thermal expansion
MDFlow
ISO 11359-2
0.000015 1/℃
Linear coefficient of thermal expansion
TDTransverse
ISO 11359-2
0.00012 1/℃
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
density
ISO 1183
1.47 g/cm³
Shrinkage rate
TDAcross Flow
ISO 294-4
0.5 %
Shrinkage rate
MDFlow
ISO 294-4
0.1 %
Water absorption rate
Saturation,23℃Saturation, 73°F
ISO 62
0.8 %
Water absorption rate
Equilibrium,23℃,50% RHEquilibrium, 73°F, 50% RH
ISO 62
0.4 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Surface resistivity
IEC 60093
-- ohms
Volume resistivity
IEC 60093
-- ohms·cm
Dielectric strength
IEC 60243-1
-- KV/mm
Compared to the anti leakage trace index
IEC 60112
V
flame retardant performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Flammability level
UL 94
HB