برگه داده فنی مقایسهOther performance شرایط آزمون روش آزمون نتیجه آزمون Elongation at Break @Break ASTM D-412 No Break % tensile strength ASTM D-624 245.9(43.1) lb/in(kN/m) Mooney viscosity ML (1+4) 125℃ ASTM D-1646 5.9 Torgue Units tensile strength @300% Elongation ASTM D-412 493(3.4) Psi(MPa) tensile strength @100% Elongation ASTM D-412 407(2.8) Psi(MPa)
Basic Performance شرایط آزمون روش آزمون نتیجه آزمون Shore hardness Shore A,15 sec ASTM D-2240 79 Shore hardness Shore D,15 sec ASTM D-2240 27 melt mass-flow rate ASTM D-1238 25 g/10 min melt mass-flow rate ASTM D-1238 10.0 g/10 min turbidity ASTM D-1003 13@50mils % density ExxonMobil Method 0.882
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature 200g ASTM D-1525 159.8(71.0) ℉(℃) Maximum melt temperature ExxonMobil Method 164.7(73.7) ℉(℃)
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap 23℃ ASTM D-256 No Break Ft-lb/in(J/m) Bending modulus 1% secant ASTM D-790 3807(26.2) Psi(MPa) Impact strength of cantilever beam gap -40℃ ASTM D-256 No Break Ft-lb/in(J/m) tensile strength @Break ASTM D-638 No Break Psi(MPa) Elongation at Break @Break ASTM D-638 No Break %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.