Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ISO 527-2/1A	14000 Mpa
tensile strength	断裂	ISO 527-2/1A/5	115 Mpa
Tensile strain	断裂	ISO 527-2/1A/5	1.4 %
Flexural modulus	23°C	ISO 178	11300 Mpa
bending strength	23°C	ISO 178	180 Mpa

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 3

injection	شرایط آزمون	روش آزمون	نتیجه آزمون
drying temperature			150 °C
drying time			3.0 hr
Suggested maximum moisture content			0.010 %
Hopper temperature			20 to 30 °C
Temperature at the rear of the barrel			355 to 365 °C
Temperature in the middle of the barrel			360 to 370 °C
Temperature at the front of the material cylinder			360 to 370 °C
Spray nozzle temperature			360 to 370 °C
Processing (melt) temperature			360 to 370 °C
Temperature			80 to 120 °C
Back pressure			< 3.00 Mpa

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	1.8 MPa, 未退火，HDT	ISO 75-2/A	295 °C
Linear coefficient of thermal expansion	流动	ISO 11359-2	6.0E-6 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向	ISO 11359-2	4.1E-5 cm/cm/°C