physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ISO 1183	1.23 g/cm³
Shrinkage rate	横向流量 : 23°C, 2.00 mm	ISO 294-4	1.0 %
Shrinkage rate	Shrinkage rate	流量 : 23°C, 2.00 mm	ISO 294-4	0.50 %
Water absorption rate	24 hr, 23°C	ISO 62	1.0 %
Water absorption rate	Water absorption rate	平衡, 23°C, 50% RH	ISO 62	2.2 %

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	0.75 mm	UL 94	HB
	UL flame retardant rating	1.5 mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	HB
Burning wire flammability index	0.75 mm	IEC 60695-2-12	675 °C
	Burning wire flammability index	1.5 mm	IEC 60695-2-12	675 °C
	Burning wire flammability index	Burning wire flammability index	3.0 mm	IEC 60695-2-12	675 °C
Hot filament ignition temperature	0.75 mm	IEC 60695-2-13	700 °C
	Hot filament ignition temperature	1.5 mm	IEC 60695-2-13	700 °C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	700 °C
Limiting Oxygen Index		ISO 4589-2	25 %

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus	23°C	ISO 527-2	6200 Mpa
tensile strength	断裂, 23°C	ISO 527-2	115 Mpa
Tensile strain	断裂, 23°C	ISO 527-2	3.0 %
Flexural modulus	23°C	ISO 178	5200 Mpa
bending strength	23°C	ISO 178	165 Mpa
Poisson's ratio		ISO 527-2	0.40

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	-30°C	ISO 179	6.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	6.0 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179	31 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	38 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180	5.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	5.1 kJ/m²

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Volume resistivity	0.750 mm	IEC 60093	1.0E+13 ohms·cm
dielectric strength	1.00 mm	IEC 60243	20 KV/mm
arc resistance	3.00 mm	ASTM D495	PLC 6
Compared to the Leakage Tracking Index (CTI)	3.00 mm	IEC 60112	V
High arc combustion index (HAI)	0.75 mm	UL 746	PLC 0
	High arc combustion index (HAI)	1.5 mm	UL 746	PLC 0
	High arc combustion index (HAI)	High arc combustion index (HAI)	3.0 mm	UL 746	PLC 0
High Voltage Arc Traceability Rate (HVTR)		UL 746	PLC 1
Hot wire ignition (HWI)	0.75 mm	UL 746	PLC 4
	Hot wire ignition (HWI)	1.5 mm	UL 746	PLC 3
	Hot wire ignition (HWI)	Hot wire ignition (HWI)	3.0 mm	UL 746	PLC 4

injection	شرایط آزمون	روش آزمون	نتیجه آزمون
drying temperature			80 °C
drying time			4.0 hr
Suggested maximum material return ratio			25 %
Temperature at the rear of the barrel			280 to 310 °C
Temperature in the middle of the barrel			280 to 310 °C
Temperature at the front of the material cylinder			280 to 310 °C
Spray nozzle temperature			280 to 310 °C
Processing (melt) temperature			285 to 305 °C
Temperature			65 to 95 °C

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45 MPa, 未退火，HDT	ISO 75-2/B	258 °C
Heat distortion temperature	Heat distortion temperature	1.8 MPa, 未退火，HDT	ISO 75-2/A	240 °C
melting temperature		ISO 11357-3	260 °C
Linear coefficient of thermal expansion	流动 : 23 到 55°C, 2.00 mm	ISO 11359-2	3.0E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向 : 23 到 55°C, 2.00 mm	ISO 11359-2	1.1E-4 cm/cm/°C
RTI Elec	0.75 mm	UL 746	140 °C
	RTI Elec	1.5 mm	UL 746	140 °C
	RTI Elec	RTI Elec	3.0 mm	UL 746	140 °C
RTI Imp	0.75 mm	UL 746	120 °C
	RTI Imp	1.5 mm	UL 746	120 °C
	RTI Imp	RTI Imp	3.0 mm	UL 746	120 °C
RTI	0.75 mm	UL 746	125 °C
	RTI	1.5 mm	UL 746	140 °C
	RTI	RTI	3.0 mm	UL 746	140 °C