Impact resistanceTest ConditionTest MethodASCEND SUZHOU/R513H NAT
Charpy Notched Impact Strength23°CISO 1796.0 kJ/m²
-30°CISO 1796.0 kJ/m²
Impact strength of cantilever beam gap23°CISO 1805.1 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 17931 kJ/m²
Impact strength of cantilever beam gap-30°CISO 1805.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 17938 kJ/m²
Mechanical propertiesTest ConditionTest MethodASCEND SUZHOU/R513H NAT
tensile strength 断裂, 23°CISO 527-2115 Mpa
Tensile strain断裂, 23°CISO 527-23.0 %
bending strength23°CISO 178165 Mpa
Flexural modulus23°CISO 1785200 Mpa
Tensile modulus23°CISO 527-26200 Mpa
Poisson's ratioISO 527-20.40
Electrical performanceTest ConditionTest MethodASCEND SUZHOU/R513H NAT
Compared to the Leakage Tracking Index (CTI)3.00 mmIEC 60112 V
Volume resistivity0.750 mmIEC 600931.0E+13 ohms·cm
dielectric strength1.00 mmIEC 6024320 KV/mm
arc resistance3.00 mmASTM D495PLC 6
High arc combustion index (HAI)3.0 mmUL 746PLC 0
Hot wire ignition (HWI)0.75 mmUL 746PLC 4
High arc combustion index (HAI)0.75 mmUL 746PLC 0
Hot wire ignition (HWI)1.5 mmUL 746PLC 3
3.0 mmUL 746PLC 4
High Voltage Arc Traceability Rate (HVTR)UL 746PLC 1
High arc combustion index (HAI)1.5 mmUL 746PLC 0
flammabilityTest ConditionTest MethodASCEND SUZHOU/R513H NAT
Hot filament ignition temperature1.5 mmIEC 60695-2-13700 °C
UL flame retardant rating3.0 mmUL 94HB
Burning wire flammability index0.75 mmIEC 60695-2-12675 °C
Hot filament ignition temperature3.0 mmIEC 60695-2-13700 °C
UL flame retardant rating0.75 mmUL 94HB
Burning wire flammability index3.0 mmIEC 60695-2-12675 °C
Hot filament ignition temperature0.75 mmIEC 60695-2-13700 °C
UL flame retardant rating1.5 mmUL 94HB
Limiting Oxygen IndexISO 4589-225 %
Burning wire flammability index1.5 mmIEC 60695-2-12675 °C
physical property Test ConditionTest MethodASCEND SUZHOU/R513H NAT
Water absorption rate平衡, 23°C, 50% RHISO 622.2 %
Shrinkage rate横向流量 : 23°C, 2.00 mmISO 294-41.0 %
流量 : 23°C, 2.00 mmISO 294-40.50 %
densityISO 11831.23 g/cm³
Water absorption rate24 hr, 23°CISO 621.0 %
Thermal performanceTest ConditionTest MethodASCEND SUZHOU/R513H NAT
RTI Elec0.75 mmUL 746140 °C
Heat distortion temperature1.8 MPa, 未退火，HDTISO 75-2/A240 °C
RTI0.75 mmUL 746125 °C
RTI Imp3.0 mmUL 746120 °C
RTI Elec1.5 mmUL 746140 °C
Linear coefficient of thermal expansion横向 : 23 到 55°C, 2.00 mmISO 11359-21.1E-4 cm/cm/°C
melting temperatureISO 11357-3260 °C
RTI Imp0.75 mmUL 746120 °C
Heat distortion temperature0.45 MPa, 未退火，HDTISO 75-2/B258 °C
Linear coefficient of thermal expansion流动 : 23 到 55°C, 2.00 mmISO 11359-23.0E-5 cm/cm/°C
RTI3.0 mmUL 746140 °C
RTI Elec3.0 mmUL 746140 °C
RTI Imp1.5 mmUL 746120 °C
RTI1.5 mmUL 746140 °C
injectionTest ConditionTest MethodASCEND SUZHOU/R513H NAT
drying time4.0 hr
Suggested maximum material return ratio25 %
Temperature in the middle of the barrel280 to 310 °C
Temperature at the rear of the barrel280 to 310 °C
Processing (melt) temperature285 to 305 °C
drying temperature80 °C
Temperature at the front of the material cylinder280 to 310 °C
Temperature65 to 95 °C
Spray nozzle temperature280 to 310 °C