برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Taber abraser ASTM D1044 14.0 mg bending strength ASTM D790 88.0 Mpa Bending modulus -- ISO 178 2350 Mpa Tensile modulus ISO 527-2 2500 Mpa Bending modulus -- ASTM D790 2450 Mpa elongation Break ISO 527-2 35 % elongation Break ASTM D638 42 % tensile strength -- ASTM D638 62.0 Mpa tensile strength Yield ISO 527-2 61.0 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Linear coefficient of thermal expansion MD ASTMD696 1E-04 cm/cm/°C Hot deformation temperature 1.8MPa,Unannealed ISO 75-2/A 91.0 °C Hot deformation temperature 1.8MPa,Unannealed ASTM D648 110 °C Hot deformation temperature 0.45MPa,Unannealed ISO 75-2/B 152 °C Hot deformation temperature 0.45MPa,Unannealed ASTM D648 158 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate 23°C,24hr,50%RH ASTM D570 0.20 % Shrinkage rate MD Internal Method 1.6-2.0 % melt mass-flow rate 190°C/2.16kg ISO 1133 9.0 g/10min
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Dielectric strength ASTM D149 19 KV/mm Volume resistivity 23°C ASTM D257 1.0E+15-1.0E+16 ohms·cm Surface resistivity ASTM D257 1.0E+16-1.0E+17 ohms Arc resistance ASTM D495 250 sec
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness M-Scale ASTM D785 80 Rockwell hardness R-Scale ASTM D785 115