POM 4563 ASAHI JAPAN
TENAC™-C
Automotive sector、Household goods、Industrial applications、Electronic field、Electrical field、Engine parts、Shell、Engineering accessories、Automotive interior parts
Medium viscosity、Weather resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | ASAHI JAPAN/4563 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 80 |
| R级 | ASTM D785 | 115 |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/4563 |
|---|---|---|---|
| Taber abraser | ASTM D1044 | 14.0 mg | |
| Tensile modulus | ISO 527-2 | 2500 Mpa | |
| elongation | 断裂 | ASTM D638 | 42 % |
| tensile strength | -- | ASTM D638 | 62.0 Mpa |
| bending strength | ASTM D790 | 88.0 Mpa | |
| Flexural modulus | -- | ISO 178 | 2350 Mpa |
| tensile strength | 屈服 | ISO 527-2 | 61.0 Mpa |
| Flexural modulus | -- | ASTM D790 | 2450 Mpa |
| elongation | 断裂 | ISO 527-2 | 35 % |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/4563 |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1.0E+16-1.0E+17 ohms | |
| Volume resistivity | 23°C | ASTM D257 | 1.0E+15-1.0E+16 ohms·cm |
| dielectric strength | ASTM D149 | 19 KV/mm | |
| arc resistance | ASTM D495 | 250 sec |
| physical property | Test Condition | Test Method | ASAHI JAPAN/4563 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.6-2.0 % |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 9.0 g/10min |
| Water absorption rate | 23°C,24hr,50%RH | ASTM D570 | 0.20 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/4563 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 110 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 158 °C | |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 152 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 91.0 °C | |
| Linear coefficient of thermal expansion | MD | ASTMD696 | 1E-04 cm/cm/°C |