Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
75 kJ/m²
Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
55 kJ/m²
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
bending strength
23°C
ISO 178
245 Mpa
Bending modulus
23°C
ISO 178/A
8500 Mpa
Tensile strain
Break,23°C
ISO 527-2/5
3.5 %
tensile strength
Break,23°C
ISO 527-2/5
145 Mpa
Tensile modulus
23°C
ISO 527-2/1
9200 Mpa
Bending strain
23°C
3.3 %
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Linear coefficient of thermal expansion
TD:23to55°C
ISO 11359-2
1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion
MD:23to55°C
ISO 11359-2
2E-05 cm/cm/°C
Melting temperature
ISO 11357-3
220 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
200 °C
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
210 °C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shrinkage rate
MD:120°C,2hr,2.00mm3
ISO 294-4
0.050 %
Shrinkage rate
MD:280°C,2.00mm2
ISO 294-4
0.25 %
Shrinkage rate
TD:120°C,2hr,2.00mm3
ISO 294-4
0.090 %
Shrinkage rate
TD:280°C,2.00mm2
ISO 294-4
0.75 %
Supplementary Information
شرایط آزمون
روش آزمون
نتیجه آزمون
ISO Shortcut
ISO 1874
PA6-HI.GR.14-100.GF30
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.