PA6 BKV130 LANXESS INDIA
Durethan®
--
High impact resistance、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | LANXESS INDIA/BKV130 |
---|---|---|---|
Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 60 kJ/m² |
23°C | ISO 180/1U | 65 kJ/m² | |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 75 kJ/m² |
-30°C | ISO 179/1eU | 55 kJ/m² |
Supplementary Information | Test Condition | Test Method | LANXESS INDIA/BKV130 |
---|---|---|---|
ISO Shortcut | ISO 1874 | PA6-HI.GR.14-100.GF30 |
Mechanical properties | Test Condition | Test Method | LANXESS INDIA/BKV130 |
---|---|---|---|
Tensile strain | 断裂,23°C | ISO 527-2/5 | 3.5 % |
Flexural modulus | 23°C | ISO 178/A | 8500 Mpa |
tensile strength | 断裂,23°C | ISO 527-2/5 | 145 Mpa |
Bending Strain | 23°C | 3.3 % | |
bending strength | 23°C | ISO 178 | 245 Mpa |
Tensile modulus | 23°C | ISO 527-2/1 | 9200 Mpa |
physical property | Test Condition | Test Method | LANXESS INDIA/BKV130 |
---|---|---|---|
Shrinkage rate | TD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.090 % |
TD:280°C,2.00mm2 | ISO 294-4 | 0.75 % | |
MD:280°C,2.00mm2 | ISO 294-4 | 0.25 % | |
MD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.050 % |
Thermal performance | Test Condition | Test Method | LANXESS INDIA/BKV130 |
---|---|---|---|
melting temperature | ISO 11357-3 | 220 °C | |
Linear coefficient of thermal expansion | MD:23到55°C | ISO 11359-2 | 2E-05 cm/cm/°C |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 210 °C |
Linear coefficient of thermal expansion | TD:23to55°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 200 °C |