برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Dart impact 23°C,3.20mm,Injection,总能量 ASTM D3763 87.0 J Suspended wall beam without notch impact strength 23°C,3.20mm,Injection ASTM D256 无断裂
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون bending strength 3.20mm,Injection ASTM D790 96.5 Mpa Bending modulus 3.20mm,Injection ASTM D790 2410 Mpa elongation Break,3.20mm,Injection ASTM D638 150 % elongation Yield,3.20mm,Injection ASTM D638 6.0 % tensile strength Break,3.20mm,Injection ASTM D638 71.0 Mpa tensile strength Yield,3.20mm,Injection ASTM D638 60.0 Mpa Tensile modulus 3.20mm,Injection ASTM D638 2410 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Linear coefficient of thermal expansion MD:-40to82°C ASTM D696 6.8E-05 cm/cm/°C Ball pressure temperature IEC 60335-1 >125 °C Vicat softening temperature ASTM D15253 148 °C Hot deformation temperature 1.8MPa,Annealed ASTM D648 140 °C Hot deformation temperature 1.8MPa,Unannealed ASTM D648 127 °C Hot deformation temperature 0.45MPa,Annealed ASTM D648 143 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 300°C/1.2kg ASTM D1238 15 g/10min Shrinkage rate MD ASTM D955 0.50-0.70 %
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Scale,3.20mm,Injection ASTM D785 118