Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
100 kJ/m²
Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
95 kJ/m²
Impact strength of cantilever beam gap
23°C
ISO 180/1A
17 kJ/m²
Impact strength of cantilever beam gap
-30°C
ISO 180/1A
15 kJ/m²
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
0.45MPaUnannealed
ISO 75-2/Bf
220 °C
Hot deformation temperature
1.80MPaAnnealed
ISO 75-2/Af
210 °C
Vicat softening temperature
Melting Temperature
ISO 11357-3
222 °C
Linear coefficient of thermal expansion
MD
ISO 11359-2
1.2E-05 cm/cm/°C
Linear coefficient of thermal expansion
TD
ISO 11359-2
9E-05 cm/cm/°C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shrinkage rate
MD2.0mm
ISO 294-4
0.19 %
Shrinkage rate
TD2.0mm
ISO 294-4
0.60 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Volume resistivity
IEC 60093
7E+14 Ω.cm
Dielectric strength
1.00mm
IEC 60243-1
35 KV/mm
Dielectric constant
23°C
IEC 60250
4.70 100HZ
Dielectric constant
23°C
IEC 60250
4.20 1MHz
Dissipation factor
23°C
IEC 60250
0.014 100HZ
Dissipation factor
23°C
IEC 60250
0.017 1MHz
Dissipation factor
相对漏电起痕指数
IEC 60112
400 V
hardness
شرایط آزمون
روش آزمون
نتیجه آزمون
Ball Pressure Test
ISO 2039-1
232 Mpa