Impact strength of simply supported beam without notch
23℃
ISO 179/1eU
55 KJ/m
Impact strength of simply supported beam without notch
-30℃
ISO 179/1eU
55 KJ/m
Charpy Notched Impact Strength
23℃
ISO 179/1eA
4.5 KJ/m
Charpy Notched Impact Strength
-30℃
ISO 179/1eA
4.5 KJ/m
Impact strength of cantilever beam gap
23℃
ISO 180/1A
4.8 KJ/m
Rockwell hardness
ISO 2039-2
79 M
Tensile modulus
1mm/min
ISO 527-2/1A
3000 Mpa
Tensile stress
50mm/min,Yield
ISO 527-2/1A
60 Mpa
Tensile modulus
50mm/min,Yield
ISO 527-2/1A
3 %
Bending modulus
23℃
ISO 178
3100 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Melting temperature
ISO 11357-1
225 °C
Glass transition temperature
ISO 11357-1
60 °C
Hot deformation temperature
1.8Mpa
ISO 75-1/-2
60 °C
Hot deformation temperature
0.45Mpa
ISO 75-1/-2
165 °C
Vicat softening temperature
ISO 306
190 °C
Linear coefficient of thermal expansion
Across Flow
ISO 11359-2
0.63 E-4/℃
Linear coefficient of thermal expansion
Across Flow
ISO 11359-2
0.77 E-4/℃
Extreme Oxygen Index
ISO 4589
30 %
UL flame retardant rating
UL 94
V-0
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
density
ISO 1183
1440 kg/m
Melt Volume Flow Rate (MVR)
ISO 1133
18 CM
Shrinkage rate
Across Flow
ISO 294-4
1.2-1.6 %
Water absorption rate
23℃,Saturation
ISO 62
0.45 %
Water absorption rate
23℃,50%相对湿度
ISO 62
0.2 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Volume resistivity
100Hz
IEC 60250
3.6
Volume resistivity
1MHz
IEC 06250
3.5
Dielectric dissipation factor
100Hz
IEC 60250
47 E-4
Dielectric dissipation factor
1MHz
IEC 60250
185 E-4
Volume resistivity
IEC 60093
1E+13 ohm.m
Surface resistivity
IEC 60093
1E+15 Ohm
Dielectric strength
IEC 60243-1
25 KV/mm